K93600 Alloy vs. Grade 8 Babbitt Metal
K93600 alloy belongs to the iron alloys classification, while grade 8 Babbitt Metal belongs to the otherwise unclassified metals. There are 11 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is grade 8 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 24 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 23 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 150 |
| Thermal Conductivity, W/m-K | 13 | |
| 24 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 24 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 10 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 11 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 1.3 |
| Stiffness to Weight: Bending, points | 21 | |
| 9.2 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 16 |