Both K93600 alloy and grade TDCrV steel are iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is grade TDCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
190
Tensile Strength: Ultimate (UTS), MPa 480 to 810
1730

Thermal Properties

Maximum Temperature: Mechanical, °C 440
410
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 520
470
Thermal Conductivity, W/m-K 13
49
Thermal Expansion, µm/m-K 7.3
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.2

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.8

Common Calculations

Stiffness to Weight: Axial, points 9.4
13
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 16 to 28
61
Strength to Weight: Bending, points 17 to 24
41
Thermal Diffusivity, mm2/s 3.1
13
Thermal Shock Resistance, points 34 to 57
51