K93600 Alloy vs. Grey Cast Iron
Both K93600 alloy and grey cast iron are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is grey cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 180 |
| Elongation at Break, % | 5.0 to 35 | |
| 9.6 |
| Shear Strength, MPa | 320 to 380 | |
| 180 to 610 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 160 to 450 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 98 to 290 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 1180 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 490 |
| Thermal Conductivity, W/m-K | 13 | |
| 46 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 8.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.5 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 13 to 37 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 27 to 240 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 5.8 to 17 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 8.7 to 17 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 13 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 6.0 to 17 |