K93600 Alloy vs. Nickel 601
K93600 alloy belongs to the iron alloys classification, while nickel 601 belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is nickel 601.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 5.0 to 35 | |
| 10 to 38 |
| Shear Strength, MPa | 320 to 380 | |
| 440 to 530 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 660 to 890 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 290 to 800 |
Thermal Properties
| Curie Temperature, °C | 250 | |
| -200 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 1100 |
| Melting Onset (Solidus), °C | 1430 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 11 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 1.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.3 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 86 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 210 to 1630 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 22 to 30 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 20 to 25 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 2.8 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 17 to 23 |