K93600 Alloy vs. SAE-AISI 1211 Steel

Both K93600 alloy and SAE-AISI 1211 steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is SAE-AISI 1211 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
190
Elongation at Break, % 5.0 to 35
11 to 29
Shear Strength, MPa 320 to 380
280 to 350
Tensile Strength: Ultimate (UTS), MPa 480 to 810
430 to 580
Tensile Strength: Yield (Proof), MPa 280 to 750
260 to 460

Thermal Properties

Maximum Temperature: Mechanical, °C 440
400
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 520
470
Thermal Conductivity, W/m-K 13
52
Thermal Expansion, µm/m-K 7.3
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.0

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.9

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
61 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
180 to 550
Stiffness to Weight: Axial, points 9.4
13
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 16 to 28
15 to 21
Strength to Weight: Bending, points 17 to 24
16 to 20
Thermal Diffusivity, mm2/s 3.1
14
Thermal Shock Resistance, points 34 to 57
14 to 18