K93600 Alloy vs. SAE-AISI 5160 Steel
Both K93600 alloy and SAE-AISI 5160 steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is SAE-AISI 5160 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Elongation at Break, % | 5.0 to 35 | |
| 12 to 18 |
| Shear Strength, MPa | 320 to 380 | |
| 390 to 700 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 660 to 1150 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 280 to 1010 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 420 |
| Melting Onset (Solidus), °C | 1430 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 43 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 8.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 73 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 200 to 2700 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 23 to 41 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 22 to 31 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 12 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 19 to 34 |