K93600 Alloy vs. SAE-AISI D5 Steel
Both K93600 alloy and SAE-AISI D5 steel are iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is SAE-AISI D5 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Elongation at Break, % | 5.0 to 35 | |
| 5.4 to 14 |
| Shear Strength, MPa | 320 to 380 | |
| 470 to 1180 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 770 to 2030 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 480 |
| Thermal Conductivity, W/m-K | 13 | |
| 27 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 4.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 4.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 28 to 73 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 24 to 46 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 7.4 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 26 to 67 |