Both K93600 alloy and SAE-AISI H12 steel are iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is SAE-AISI H12 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
190
Tensile Strength: Ultimate (UTS), MPa 480 to 810
690 to 1850

Thermal Properties

Melting Onset (Solidus), °C 1430
1440
Specific Heat Capacity, J/kg-K 520
470
Thermal Conductivity, W/m-K 13
36
Thermal Expansion, µm/m-K 7.3
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
8.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.5

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.9

Common Calculations

Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 16 to 28
24 to 65
Strength to Weight: Bending, points 17 to 24
22 to 42
Thermal Diffusivity, mm2/s 3.1
9.8
Thermal Shock Resistance, points 34 to 57
22 to 60