K93600 Alloy vs. Type 2 Magnetic Alloy
Both K93600 alloy and Type 2 magnetic alloy are iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is Type 2 magnetic alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Elongation at Break, % | 5.0 to 35 | |
2.0 to 38 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
510 to 910 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
260 to 870 |
Thermal Properties
Curie Temperature, °C | 250 | |
480 |
Melting Onset (Solidus), °C | 1430 | |
1370 |
Specific Heat Capacity, J/kg-K | 520 | |
460 |
Thermal Expansion, µm/m-K | 7.3 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
3.9 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
4.2 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
8.4 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
18 to 160 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
170 to 2010 |
Stiffness to Weight: Axial, points | 9.4 | |
12 |
Stiffness to Weight: Bending, points | 21 | |
23 |
Strength to Weight: Axial, points | 16 to 28 | |
17 to 30 |
Strength to Weight: Bending, points | 17 to 24 | |
17 to 25 |
Thermal Shock Resistance, points | 34 to 57 | |
16 to 29 |