K93600 Alloy vs. C17000 Copper
K93600 alloy belongs to the iron alloys classification, while C17000 copper belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is C17000 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 120 |
| Elongation at Break, % | 5.0 to 35 | |
| 1.1 to 31 |
| Shear Strength, MPa | 320 to 380 | |
| 320 to 750 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 490 to 1310 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 160 to 1140 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 270 |
| Melting Onset (Solidus), °C | 1430 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 390 |
| Thermal Conductivity, W/m-K | 13 | |
| 110 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 22 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 4.2 to 390 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 110 to 5420 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 21 | |
| 19 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 15 to 41 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 16 to 30 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 32 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 17 to 45 |