K93600 Alloy vs. C35600 Brass
K93600 alloy belongs to the iron alloys classification, while C35600 brass belongs to the copper alloys. There are 16 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is C35600 brass.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
100 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
340 to 650 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 440 | |
120 |
Melting Onset (Solidus), °C | 1430 | |
890 |
Specific Heat Capacity, J/kg-K | 520 | |
380 |
Thermal Conductivity, W/m-K | 13 | |
120 |
Thermal Expansion, µm/m-K | 7.3 | |
21 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
26 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
29 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
8.1 |
Common Calculations
Stiffness to Weight: Axial, points | 9.4 | |
7.0 |
Stiffness to Weight: Bending, points | 21 | |
19 |
Strength to Weight: Axial, points | 16 to 28 | |
11 to 22 |
Strength to Weight: Bending, points | 17 to 24 | |
13 to 21 |
Thermal Diffusivity, mm2/s | 3.1 | |
38 |
Thermal Shock Resistance, points | 34 to 57 | |
11 to 22 |