K93600 Alloy vs. C71500 Copper-nickel
K93600 alloy belongs to the iron alloys classification, while C71500 copper-nickel belongs to the copper alloys. There are 16 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is C71500 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 140 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 380 to 620 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 260 |
| Melting Onset (Solidus), °C | 1430 | |
| 1170 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 400 |
| Thermal Conductivity, W/m-K | 13 | |
| 28 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 4.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 4.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 21 | |
| 19 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 7.7 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 12 to 20 |