K93600 Alloy vs. R60901 Alloy
K93600 alloy belongs to the iron alloys classification, while R60901 alloy belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is R60901 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 98 |
| Elongation at Break, % | 5.0 to 35 | |
| 17 to 22 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 500 to 580 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 350 to 390 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 520 | |
| 270 |
| Thermal Conductivity, W/m-K | 13 | |
| 17 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 6.6 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 88 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 640 to 760 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 9.7 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 58 to 67 |