K93600 Alloy vs. S17600 Stainless Steel
Both K93600 alloy and S17600 stainless steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is S17600 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 5.0 to 35 | |
| 8.6 to 11 |
| Shear Strength, MPa | 320 to 380 | |
| 560 to 880 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 940 to 1490 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 580 to 1310 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 890 |
| Melting Onset (Solidus), °C | 1430 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 480 |
| Thermal Conductivity, W/m-K | 13 | |
| 15 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 2.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 70 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 850 to 4390 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 34 to 54 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 28 to 37 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 4.1 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 31 to 50 |