K93600 Alloy vs. S21600 Stainless Steel

Both K93600 alloy and S21600 stainless steel are iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is S21600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
200
Elongation at Break, % 5.0 to 35
46
Shear Strength, MPa 320 to 380
500
Tensile Strength: Ultimate (UTS), MPa 480 to 810
710
Tensile Strength: Yield (Proof), MPa 280 to 750
390

Thermal Properties

Maximum Temperature: Mechanical, °C 440
990
Melting Onset (Solidus), °C 1430
1380
Specific Heat Capacity, J/kg-K 520
480
Thermal Expansion, µm/m-K 7.3
17

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.7

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
270
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
370
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 16 to 28
25
Strength to Weight: Bending, points 17 to 24
23
Thermal Shock Resistance, points 34 to 57
15