K93600 Alloy vs. S46910 Stainless Steel
Both K93600 alloy and S46910 stainless steel are iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is S46910 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 5.0 to 35 | |
| 2.2 to 11 |
| Shear Strength, MPa | 320 to 380 | |
| 410 to 1410 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 680 to 2470 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 450 to 2290 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 810 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 470 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 48 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 510 to 4780 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 24 to 86 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 22 to 51 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 23 to 84 |