MakeItFrom.com
Menu (ESC)

K93603 Alloy vs. EN 1.0060 Steel

Both K93603 alloy and EN 1.0060 steel are iron alloys. They have 63% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is K93603 alloy and the bottom bar is EN 1.0060 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 490 to 810
630

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1430
1470
Melting Onset (Solidus), °C 1380
1430
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 25
1.7
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 4.8
1.4
Embodied Energy, MJ/kg 66
18
Embodied Water, L/kg 120
45

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 17 to 27
22
Strength to Weight: Bending, points 17 to 24
21
Thermal Shock Resistance, points 15 to 25
20

Alloy Composition

Aluminum (Al), % 0 to 0.1
0
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 0 to 0.25
0
Cobalt (Co), % 0 to 0.5
0
Iron (Fe), % 61.8 to 64
99.876 to 100
Magnesium (Mg), % 0 to 0.1
0
Manganese (Mn), % 0 to 0.6
0
Nickel (Ni), % 36
0
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.015
0 to 0.055
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.015
0 to 0.055
Titanium (Ti), % 0 to 0.1
0
Zirconium (Zr), % 0 to 0.1
0