Both K94200 alloy and SAE-AISI H26 steel are iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is K94200 alloy and the bottom bar is SAE-AISI H26 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
210
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 54
80
Tensile Strength: Ultimate (UTS), MPa 500 to 710
720 to 2100

Thermal Properties

Melting Onset (Solidus), °C 1440
1760
Specific Heat Capacity, J/kg-K 500
410
Thermal Conductivity, W/m-K 15
22
Thermal Expansion, µm/m-K 5.0
12

Otherwise Unclassified Properties

Density, g/cm3 8.2
9.3

Common Calculations

Stiffness to Weight: Axial, points 9.8
12
Stiffness to Weight: Bending, points 21
21
Strength to Weight: Axial, points 17 to 24
22 to 63
Strength to Weight: Bending, points 17 to 22
19 to 39
Thermal Diffusivity, mm2/s 3.7
5.6
Thermal Shock Resistance, points 49 to 70
22 to 63

Comparable Variants