N06035 Nickel vs. SAE-AISI H22 Steel

N06035 nickel belongs to the nickel alloys classification, while SAE-AISI H22 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is N06035 nickel and the bottom bar is SAE-AISI H22 steel.

UNS N06035 (2.4643) Nickel-Chromium Alloy SAE-AISI H22 (T20822) Tungsten Hot-Work Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		84
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		660
Tensile Strength: Ultimate (UTS), MPa		700 to 1920

Thermal Properties

Latent Heat of Fusion, J/g		340
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		1440
Melting Completion (Liquidus), °C		1670

Melting Onset (Solidus), °C		1390
Melting Onset (Solidus), °C		1620

Specific Heat Capacity, J/kg-K		450
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		60
Base Metal Price, % relative		28

Density, g/cm³		8.4
Density, g/cm³		8.7

Embodied Carbon, kg CO₂/kg material		10
Embodied Carbon, kg CO₂/kg material		4.9

Embodied Energy, MJ/kg		140
Embodied Energy, MJ/kg		73

Embodied Water, L/kg		330
Embodied Water, L/kg		72

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		22 to 61

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		20 to 39

Thermal Shock Resistance, points		17
Thermal Shock Resistance, points		22 to 60

Alloy Composition

Aluminum (Al), %		0 to 0.4
Aluminum (Al), %		0

Carbon (C), %		0 to 0.050
Carbon (C), %		0.3 to 0.4

Chromium (Cr), %		32.3 to 34.3
Chromium (Cr), %		1.8 to 3.8

Cobalt (Co), %		0 to 1.0
Cobalt (Co), %		0

Copper (Cu), %		0 to 0.3
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 2.0
Iron (Fe), %		82.2 to 87.4

Manganese (Mn), %		0 to 0.5
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		7.6 to 9.0
Molybdenum (Mo), %		0

Nickel (Ni), %		51.1 to 60.2
Nickel (Ni), %		0 to 0.3

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.6
Silicon (Si), %		0.15 to 0.4

Sulfur (S), %		0 to 0.015
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0 to 0.6
Tungsten (W), %		10 to 11.8

Vanadium (V), %		0 to 0.2
Vanadium (V), %		0.25 to 0.5