N06200 Nickel vs. 88-silver 12-tin-oxide
N06200 nickel belongs to the nickel alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is N06200 nickel and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.3 | |
| 84 to 86 |
| Elongation at Break, % | 51 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
| 24 to 70 |
| Shear Strength, MPa | 560 | |
| 150 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 780 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 320 | |
| 110 to 260 |