MakeItFrom.com
Menu (ESC)

N06200 Nickel vs. ASTM B477 Au-Ni-Ag

N06200 nickel belongs to the nickel alloys classification, while ASTM B477 Au-Ni-Ag belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is ASTM B477 Au-Ni-Ag.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
95
Elongation at Break, % 51
5.5 to 11
Poisson's Ratio 0.29
0.41
Shear Modulus, GPa 84
34
Shear Strength, MPa 560
190 to 320
Tensile Strength: Ultimate (UTS), MPa 780
310 to 550

Thermal Properties

Latent Heat of Fusion, J/g 330
80
Melting Completion (Liquidus), °C 1500
1010
Melting Onset (Solidus), °C 1450
930
Specific Heat Capacity, J/kg-K 430
160
Thermal Expansion, µm/m-K 12
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
14
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
7.5

Otherwise Unclassified Properties

Density, g/cm3 8.7
17

Common Calculations

Stiffness to Weight: Axial, points 14
3.1
Stiffness to Weight: Bending, points 23
8.9
Strength to Weight: Axial, points 25
5.0 to 9.0
Strength to Weight: Bending, points 22
6.0 to 8.8
Thermal Shock Resistance, points 21
16 to 28

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.5
0
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 22 to 24
0
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
0
Gold (Au), % 0
74.2 to 75.8
Iron (Fe), % 0 to 3.0
0
Manganese (Mn), % 0 to 0.010
0
Molybdenum (Mo), % 15 to 17
0
Nickel (Ni), % 51 to 61.7
2.6 to 3.4
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.080
0
Silver (Ag), % 0
21.4 to 22.6
Sulfur (S), % 0 to 0.010
0
Residuals, % 0
0 to 0.3