N06200 Nickel vs. ASTM B631 Class C

N06200 nickel belongs to the nickel alloys classification, while ASTM B631 class C belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is ASTM B631 class C.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
180 to 190
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 84
66 to 71

Thermal Properties

Latent Heat of Fusion, J/g 330
140 to 150
Melting Completion (Liquidus), °C 1500
2090 to 2230
Specific Heat Capacity, J/kg-K 430
180
Thermal Conductivity, W/m-K 9.1
450 to 490
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
55 to 63
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
36 to 43

Otherwise Unclassified Properties

Density, g/cm3 8.7
13 to 14
Embodied Carbon, kg CO2/kg material 12
55 to 59
Embodied Energy, MJ/kg 160
860 to 920

Common Calculations

Stiffness to Weight: Axial, points 14
7.4 to 7.6
Stiffness to Weight: Bending, points 23
14
Thermal Diffusivity, mm2/s 2.4
180 to 200