N06200 Nickel vs. AWS BAg-8a

N06200 nickel belongs to the nickel alloys classification, while AWS BAg-8a belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is AWS BAg-8a.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
83
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 84
31
Tensile Strength: Ultimate (UTS), MPa 780
150

Thermal Properties

Latent Heat of Fusion, J/g 330
140
Melting Completion (Liquidus), °C 1500
770
Melting Onset (Solidus), °C 1450
770
Specific Heat Capacity, J/kg-K 430
290
Thermal Expansion, µm/m-K 12
19

Otherwise Unclassified Properties

Density, g/cm3 8.7
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.6
Stiffness to Weight: Bending, points 23
15
Strength to Weight: Axial, points 25
4.2
Strength to Weight: Bending, points 22
6.3
Thermal Shock Resistance, points 21
6.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.5
0
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 22 to 24
0
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
26.4 to 28.8
Iron (Fe), % 0 to 3.0
0
Lithium (Li), % 0
0.25 to 0.5
Manganese (Mn), % 0 to 0.010
0
Molybdenum (Mo), % 15 to 17
0
Nickel (Ni), % 51 to 61.7
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.080
0
Silver (Ag), % 0
71 to 73
Sulfur (S), % 0 to 0.010
0
Residuals, % 0
0 to 0.15