N06200 nickel belongs to the nickel alloys classification, while AWS BVAg-31 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is AWS BVAg-31.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
90
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 84
33
Tensile Strength: Ultimate (UTS), MPa 780
180

Thermal Properties

Latent Heat of Fusion, J/g 330
150
Melting Completion (Liquidus), °C 1500
850
Melting Onset (Solidus), °C 1450
820
Specific Heat Capacity, J/kg-K 430
280
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Density, g/cm3 8.7
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.9
Stiffness to Weight: Bending, points 23
15
Strength to Weight: Axial, points 25
4.9
Strength to Weight: Bending, points 22
7.0
Thermal Shock Resistance, points 21
7.8

Alloy Composition

Aluminum (Al), % 0 to 0.5
0
Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.010
0 to 0.0050
Chromium (Cr), % 22 to 24
0
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
31 to 33
Iron (Fe), % 0 to 3.0
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 0 to 0.010
0
Molybdenum (Mo), % 15 to 17
0
Nickel (Ni), % 51 to 61.7
0
Palladium (Pd), % 0
8.0 to 12
Phosphorus (P), % 0 to 0.025
0 to 0.0020
Silicon (Si), % 0 to 0.080
0
Silver (Ag), % 0
57 to 59
Sulfur (S), % 0 to 0.010
0
Zinc (Zn), % 0
0 to 0.0010