N06200 Nickel vs. EN 1.4889 Cast Nickel

Both N06200 nickel and EN 1.4889 cast nickel are nickel alloys. They have 69% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is EN 1.4889 cast nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 51
3.4
Fatigue Strength, MPa 290
110
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 84
79
Tensile Strength: Ultimate (UTS), MPa 780
500
Tensile Strength: Yield (Proof), MPa 320
270

Thermal Properties

Latent Heat of Fusion, J/g 330
350
Maximum Temperature: Mechanical, °C 990
1160
Melting Completion (Liquidus), °C 1500
1360
Melting Onset (Solidus), °C 1450
1320
Specific Heat Capacity, J/kg-K 430
480
Thermal Expansion, µm/m-K 12
14

Otherwise Unclassified Properties

Base Metal Price, % relative 65
55
Density, g/cm3 8.7
7.9
Embodied Carbon, kg CO2/kg material 12
8.5
Embodied Energy, MJ/kg 160
120
Embodied Water, L/kg 310
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 320
14
Resilience: Unit (Modulus of Resilience), kJ/m3 240
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 25
18
Strength to Weight: Bending, points 22
18
Thermal Shock Resistance, points 21
13

Alloy Composition

Aluminum (Al), % 0 to 0.5
0
Carbon (C), % 0 to 0.010
0.35 to 0.45
Chromium (Cr), % 22 to 24
32.5 to 37.5
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
0
Iron (Fe), % 0 to 3.0
10.5 to 21.2
Manganese (Mn), % 0 to 0.010
1.0 to 1.5
Molybdenum (Mo), % 15 to 17
0
Nickel (Ni), % 51 to 61.7
42 to 46
Niobium (Nb), % 0
1.5 to 2.0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.080
1.5 to 2.0
Sulfur (S), % 0 to 0.010
0 to 0.030