N06200 Nickel vs. Grade 705C Zirconium

N06200 nickel belongs to the nickel alloys classification, while grade 705C zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is grade 705C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
98
Elongation at Break, % 51
13
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 84
36
Tensile Strength: Ultimate (UTS), MPa 780
540
Tensile Strength: Yield (Proof), MPa 320
390

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Specific Heat Capacity, J/kg-K 430
270
Thermal Conductivity, W/m-K 9.1
18
Thermal Expansion, µm/m-K 12
5.7

Otherwise Unclassified Properties

Density, g/cm3 8.7
6.7
Embodied Water, L/kg 310
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 320
66
Resilience: Unit (Modulus of Resilience), kJ/m3 240
790
Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 25
22
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 2.4
9.9
Thermal Shock Resistance, points 21
69

Alloy Composition

Aluminum (Al), % 0 to 0.5
0
Carbon (C), % 0 to 0.010
0 to 0.1
Chromium (Cr), % 22 to 24
0
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0 to 3.0
0 to 0.3
Manganese (Mn), % 0 to 0.010
0
Molybdenum (Mo), % 15 to 17
0
Nickel (Ni), % 51 to 61.7
0
Niobium (Nb), % 0
2.0 to 3.0
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.010
Silicon (Si), % 0 to 0.080
0
Sulfur (S), % 0 to 0.010
0
Zirconium (Zr), % 0
91.9 to 98