N06200 Nickel vs. Solder Alloy 102

N06200 nickel belongs to the nickel alloys classification, while solder alloy 102 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is solder alloy 102.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
38
Elongation at Break, % 51
48
Poisson's Ratio 0.29
0.39
Shear Modulus, GPa 84
14
Tensile Strength: Ultimate (UTS), MPa 780
31

Thermal Properties

Latent Heat of Fusion, J/g 330
46
Melting Completion (Liquidus), °C 1500
180
Melting Onset (Solidus), °C 1450
180
Specific Heat Capacity, J/kg-K 430
190
Thermal Conductivity, W/m-K 9.1
53
Thermal Expansion, µm/m-K 12
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
12
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
13

Otherwise Unclassified Properties

Density, g/cm3 8.7
8.8
Embodied Carbon, kg CO2/kg material 12
11
Embodied Energy, MJ/kg 160
180
Embodied Water, L/kg 310
930

Common Calculations

Stiffness to Weight: Axial, points 14
2.4
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 25
1.0
Strength to Weight: Bending, points 22
2.5
Thermal Diffusivity, mm2/s 2.4
32
Thermal Shock Resistance, points 21
2.4

Alloy Composition

Aluminum (Al), % 0 to 0.5
0 to 0.0010
Antimony (Sb), % 0
0 to 0.050
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.050
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 22 to 24
0
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 3.0
0 to 0.020
Lead (Pb), % 0
36 to 37.5
Manganese (Mn), % 0 to 0.010
0
Molybdenum (Mo), % 15 to 17
0
Nickel (Ni), % 51 to 61.7
0 to 0.010
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.080
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
62.5 to 63.5
Zinc (Zn), % 0
0 to 0.0010