N06200 Nickel vs. Solder Alloy 135

N06200 nickel belongs to the nickel alloys classification, while solder alloy 135 belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is solder alloy 135.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
27
Elongation at Break, % 51
20
Poisson's Ratio 0.29
0.41
Shear Modulus, GPa 84
9.5
Tensile Strength: Ultimate (UTS), MPa 780
35

Thermal Properties

Latent Heat of Fusion, J/g 330
36
Melting Completion (Liquidus), °C 1500
250
Melting Onset (Solidus), °C 1450
190
Specific Heat Capacity, J/kg-K 430
160
Thermal Conductivity, W/m-K 9.1
42
Thermal Expansion, µm/m-K 12
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
9.5
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 65
90
Density, g/cm3 8.7
10
Embodied Carbon, kg CO2/kg material 12
7.3
Embodied Energy, MJ/kg 160
120
Embodied Water, L/kg 310
720

Common Calculations

Stiffness to Weight: Axial, points 14
1.5
Stiffness to Weight: Bending, points 23
9.9
Strength to Weight: Axial, points 25
1.0
Strength to Weight: Bending, points 22
2.4
Thermal Diffusivity, mm2/s 2.4
27
Thermal Shock Resistance, points 21
3.5

Alloy Composition

Aluminum (Al), % 0 to 0.5
0 to 0.0010
Antimony (Sb), % 0
0.5 to 1.8
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 22 to 24
0
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 3.0
0 to 0.020
Lead (Pb), % 0
67.1 to 70
Manganese (Mn), % 0 to 0.010
0
Molybdenum (Mo), % 15 to 17
0
Nickel (Ni), % 51 to 61.7
0 to 0.010
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.080
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
29.5 to 30.5
Zinc (Zn), % 0
0 to 0.0010