MakeItFrom.com
Menu (ESC)

N06200 Nickel vs. Solder Alloy 704

N06200 nickel belongs to the nickel alloys classification, while solder alloy 704 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is solder alloy 704.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
51
Elongation at Break, % 51
30
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 84
19
Tensile Strength: Ultimate (UTS), MPa 780
55

Thermal Properties

Latent Heat of Fusion, J/g 330
62
Melting Completion (Liquidus), °C 1500
240
Melting Onset (Solidus), °C 1450
220
Specific Heat Capacity, J/kg-K 430
220
Thermal Conductivity, W/m-K 9.1
50
Thermal Expansion, µm/m-K 12
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
13
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
15

Otherwise Unclassified Properties

Density, g/cm3 8.7
7.5
Embodied Carbon, kg CO2/kg material 12
19
Embodied Energy, MJ/kg 160
320

Common Calculations

Stiffness to Weight: Axial, points 14
3.8
Stiffness to Weight: Bending, points 23
17
Strength to Weight: Axial, points 25
2.1
Strength to Weight: Bending, points 22
4.3
Thermal Diffusivity, mm2/s 2.4
30
Thermal Shock Resistance, points 21
3.5

Alloy Composition

Aluminum (Al), % 0 to 0.5
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 22 to 24
0
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 3.0
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0 to 0.010
0
Molybdenum (Mo), % 15 to 17
0
Nickel (Ni), % 51 to 61.7
0 to 0.010
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.080
0
Silver (Ag), % 0
4.8 to 5.2
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
94.3 to 95.2
Zinc (Zn), % 0
0 to 0.0010