N06200 Nickel vs. Type 2 Niobium

N06200 nickel belongs to the nickel alloys classification, while Type 2 niobium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is Type 2 niobium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 51
29
Poisson's Ratio 0.29
0.4
Shear Modulus, GPa 84
38
Tensile Strength: Ultimate (UTS), MPa 780
140
Tensile Strength: Yield (Proof), MPa 320
82

Thermal Properties

Latent Heat of Fusion, J/g 330
320
Specific Heat Capacity, J/kg-K 430
270
Thermal Conductivity, W/m-K 9.1
52
Thermal Expansion, µm/m-K 12
7.3

Otherwise Unclassified Properties

Density, g/cm3 8.7
8.6
Embodied Water, L/kg 310
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 320
35
Resilience: Unit (Modulus of Resilience), kJ/m3 240
32
Stiffness to Weight: Axial, points 14
6.8
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 25
4.6
Strength to Weight: Bending, points 22
7.1
Thermal Diffusivity, mm2/s 2.4
23
Thermal Shock Resistance, points 21
13

Alloy Composition

Aluminum (Al), % 0 to 0.5
0
Carbon (C), % 0 to 0.010
0 to 0.010
Chromium (Cr), % 22 to 24
0
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
0
Hafnium (Hf), % 0
0 to 0.020
Hydrogen (H), % 0
0 to 0.0015
Iron (Fe), % 0 to 3.0
0 to 0.010
Manganese (Mn), % 0 to 0.010
0
Molybdenum (Mo), % 15 to 17
0 to 0.020
Nickel (Ni), % 51 to 61.7
0 to 0.0050
Niobium (Nb), % 0
99.5 to 100
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.025
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.080
0 to 0.0050
Sulfur (S), % 0 to 0.010
0
Tantalum (Ta), % 0
0 to 0.3
Titanium (Ti), % 0
0 to 0.030
Tungsten (W), % 0
0 to 0.050
Zirconium (Zr), % 0
0 to 0.020