N06200 Nickel vs. Z21210 Zinc

N06200 nickel belongs to the nickel alloys classification, while Z21210 zinc belongs to the zinc alloys. There are 12 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is Z21210 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Tensile Strength: Ultimate (UTS), MPa 780
150 to 170

Thermal Properties

Melting Completion (Liquidus), °C 1500
420
Melting Onset (Solidus), °C 1450
420
Specific Heat Capacity, J/kg-K 430
400
Thermal Conductivity, W/m-K 9.1
110
Thermal Expansion, µm/m-K 12
32

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
28
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
35

Otherwise Unclassified Properties

Density, g/cm3 8.7
7.1

Common Calculations

Strength to Weight: Axial, points 25
5.7 to 6.4
Strength to Weight: Bending, points 22
8.6 to 9.4
Thermal Diffusivity, mm2/s 2.4
38