N06210 Nickel vs. ZA-8
N06210 nickel belongs to the nickel alloys classification, while ZA-8 belongs to the zinc alloys. There are 26 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is N06210 nickel and the bottom bar is ZA-8.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 220 | |
85 to 86 |
Elongation at Break, % | 51 | |
1.3 to 8.0 |
Fatigue Strength, MPa | 320 | |
51 to 100 |
Poisson's Ratio | 0.29 | |
0.26 |
Shear Modulus, GPa | 85 | |
34 |
Shear Strength, MPa | 560 | |
240 to 280 |
Tensile Strength: Ultimate (UTS), MPa | 780 | |
210 to 370 |
Tensile Strength: Yield (Proof), MPa | 350 | |
210 to 290 |
Thermal Properties
Latent Heat of Fusion, J/g | 330 | |
110 |
Maximum Temperature: Mechanical, °C | 980 | |
100 |
Melting Completion (Liquidus), °C | 1570 | |
400 |
Melting Onset (Solidus), °C | 1510 | |
380 |
Specific Heat Capacity, J/kg-K | 420 | |
440 |
Thermal Expansion, µm/m-K | 12 | |
23 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 85 | |
11 |
Density, g/cm3 | 9.0 | |
6.3 |
Embodied Carbon, kg CO2/kg material | 17 | |
3.3 |
Embodied Energy, MJ/kg | 250 | |
62 |
Embodied Water, L/kg | 310 | |
420 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
2.8 to 28 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 | |
260 to 490 |
Stiffness to Weight: Axial, points | 14 | |
7.5 |
Stiffness to Weight: Bending, points | 22 | |
23 |
Strength to Weight: Axial, points | 24 | |
9.3 to 17 |
Strength to Weight: Bending, points | 21 | |
12 to 18 |
Thermal Shock Resistance, points | 22 | |
7.6 to 13 |
Alloy Composition
Aluminum (Al), % | 0 | |
8.0 to 8.8 |
Cadmium (Cd), % | 0 | |
0 to 0.0060 |
Carbon (C), % | 0 to 0.015 | |
0 |
Chromium (Cr), % | 18 to 20 | |
0 |
Cobalt (Co), % | 0 to 1.0 | |
0 |
Copper (Cu), % | 0 | |
0.8 to 1.3 |
Iron (Fe), % | 0 to 1.0 | |
0 to 0.075 |
Lead (Pb), % | 0 | |
0 to 0.0060 |
Magnesium (Mg), % | 0 | |
0.015 to 0.030 |
Manganese (Mn), % | 0 to 0.5 | |
0 |
Molybdenum (Mo), % | 18 to 20 | |
0 |
Nickel (Ni), % | 54.8 to 62.5 | |
0 to 0.020 |
Phosphorus (P), % | 0 to 0.020 | |
0 |
Silicon (Si), % | 0 to 0.080 | |
0 to 0.045 |
Sulfur (S), % | 0 to 0.020 | |
0 |
Tantalum (Ta), % | 1.5 to 2.2 | |
0 |
Tin (Sn), % | 0 | |
0 to 0.0030 |
Vanadium (V), % | 0 to 0.35 | |
0 |
Zinc (Zn), % | 0 | |
89.7 to 91.2 |