N06250 Nickel vs. EN 1.8522 Steel
N06250 nickel belongs to the nickel alloys classification, while EN 1.8522 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N06250 nickel and the bottom bar is EN 1.8522 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 82 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 730 to 1250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 470 |
| Melting Completion (Liquidus), °C | 1490 | |
| 1460 |
| Melting Onset (Solidus), °C | 1440 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 4.2 |
| Density, g/cm3 | 8.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 2.2 |
| Embodied Energy, MJ/kg | 140 | |
| 31 |
| Embodied Water, L/kg | 270 | |
| 63 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 23 | |
| 26 to 44 |
| Strength to Weight: Bending, points | 21 | |
| 23 to 33 |
| Thermal Shock Resistance, points | 19 | |
| 21 to 36 |
Alloy Composition
| Carbon (C), % | 0 to 0.020 | |
| 0.29 to 0.36 |
| Chromium (Cr), % | 20 to 23 | |
| 2.8 to 3.3 |
| Copper (Cu), % | 0.25 to 1.3 | |
| 0 to 0.1 |
| Iron (Fe), % | 7.4 to 19.4 | |
| 93.7 to 96 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.4 to 0.7 |
| Molybdenum (Mo), % | 10.1 to 12 | |
| 0.7 to 1.2 |
| Nickel (Ni), % | 50 to 54 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.090 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.035 |
| Tungsten (W), % | 0.25 to 1.3 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.25 |