N06455 Nickel vs. AWS BNi-8

Both N06455 nickel and AWS BNi-8 are nickel alloys. They have 66% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is N06455 nickel and the bottom bar is AWS BNi-8.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
180
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 82
67
Tensile Strength: Ultimate (UTS), MPa 780
570

Thermal Properties

Latent Heat of Fusion, J/g 320
390
Melting Completion (Liquidus), °C 1510
1010
Melting Onset (Solidus), °C 1450
980
Specific Heat Capacity, J/kg-K 430
480
Thermal Expansion, µm/m-K 11
13

Otherwise Unclassified Properties

Base Metal Price, % relative 65
46
Density, g/cm3 8.8
7.9
Embodied Carbon, kg CO2/kg material 12
8.2
Embodied Energy, MJ/kg 160
120
Embodied Water, L/kg 290
220

Common Calculations

Stiffness to Weight: Axial, points 13
12
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
20
Strength to Weight: Bending, points 21
19
Thermal Shock Resistance, points 24
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.015
0 to 0.060
Chromium (Cr), % 14 to 18
0
Cobalt (Co), % 0 to 2.0
0 to 0.1
Copper (Cu), % 0
4.0 to 5.0
Iron (Fe), % 0 to 3.0
0
Manganese (Mn), % 0 to 1.0
21.5 to 24.5
Molybdenum (Mo), % 14 to 17
0
Nickel (Ni), % 58.1 to 72
61.6 to 68.5
Phosphorus (P), % 0 to 0.040
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 0.080
6.0 to 8.0
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0 to 0.7
0 to 0.050
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5