N06455 Nickel vs. EN 2.4665 Nickel

Both N06455 nickel and EN 2.4665 nickel are nickel alloys. Both are furnished in the solution annealed (AT) condition. They have 75% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is N06455 nickel and the bottom bar is EN 2.4665 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
210
Elongation at Break, % 47
34
Fatigue Strength, MPa 290
220
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 82
81
Shear Strength, MPa 550
520
Tensile Strength: Ultimate (UTS), MPa 780
790
Tensile Strength: Yield (Proof), MPa 330
300

Thermal Properties

Latent Heat of Fusion, J/g 320
320
Maximum Temperature: Mechanical, °C 960
990
Melting Completion (Liquidus), °C 1510
1460
Melting Onset (Solidus), °C 1450
1410
Specific Heat Capacity, J/kg-K 430
450
Thermal Conductivity, W/m-K 10
12
Thermal Expansion, µm/m-K 11
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 65
55
Density, g/cm3 8.8
8.4
Embodied Carbon, kg CO2/kg material 12
9.2
Embodied Energy, MJ/kg 160
130
Embodied Water, L/kg 290
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 300
210
Resilience: Unit (Modulus of Resilience), kJ/m3 260
220
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 24
26
Strength to Weight: Bending, points 21
22
Thermal Diffusivity, mm2/s 2.7
3.2
Thermal Shock Resistance, points 24
20

Alloy Composition

Aluminum (Al), % 0
0 to 0.5
Boron (B), % 0
0 to 0.010
Carbon (C), % 0 to 0.015
0.050 to 0.15
Chromium (Cr), % 14 to 18
20.5 to 23
Cobalt (Co), % 0 to 2.0
0.5 to 2.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 0 to 3.0
17 to 20
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 14 to 17
8.0 to 10
Nickel (Ni), % 58.1 to 72
40.3 to 53.8
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 0.080
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0 to 0.7
0
Tungsten (W), % 0
0.2 to 1.0