N07041 Nickel vs. AISI 440C Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while AISI 440C stainless steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is AISI 440C stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 14 | |
| 2.0 to 14 |
| Fatigue Strength, MPa | 540 | |
| 260 to 840 |
| Shear Strength, MPa | 850 | |
| 430 to 1120 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 710 to 1970 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 450 to 1900 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 22 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 39 to 88 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 47 | |
| 26 to 71 |
| Strength to Weight: Bending, points | 34 | |
| 23 to 46 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 6.0 |
| Thermal Shock Resistance, points | 38 | |
| 26 to 71 |