N07041 Nickel vs. EN 1.7362 Steel
N07041 nickel belongs to the nickel alloys classification, while EN 1.7362 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.7362 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 21 to 22 |
| Fatigue Strength, MPa | 540 | |
| 140 to 250 |
| Shear Strength, MPa | 850 | |
| 320 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 510 to 600 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 200 to 360 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 40 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 90 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 100 to 340 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 47 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 34 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 11 |
| Thermal Shock Resistance, points | 38 | |
| 14 to 17 |