N07041 Nickel vs. Grade 5 Titanium
N07041 nickel belongs to the nickel alloys classification, while grade 5 titanium belongs to the titanium alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is grade 5 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 110 |
| Elongation at Break, % | 14 | |
| 8.6 to 11 |
| Fatigue Strength, MPa | 540 | |
| 530 to 630 |
| Shear Strength, MPa | 850 | |
| 600 to 710 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 1000 to 1190 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 910 to 1110 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1650 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 560 |
| Thermal Conductivity, W/m-K | 11 | |
| 6.8 |
| Thermal Expansion, µm/m-K | 12 | |
| 8.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 4.4 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 100 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 3980 to 5880 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 35 |
| Strength to Weight: Axial, points | 47 | |
| 62 to 75 |
| Strength to Weight: Bending, points | 34 | |
| 50 to 56 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 2.7 |
| Thermal Shock Resistance, points | 38 | |
| 76 to 91 |