N07041 nickel belongs to the nickel alloys classification, while grade 9 titanium belongs to the titanium alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is grade 9 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 14
11 to 17
Fatigue Strength, MPa 540
330 to 480
Shear Strength, MPa 850
430 to 580
Tensile Strength: Ultimate (UTS), MPa 1400
700 to 960
Tensile Strength: Yield (Proof), MPa 1050
540 to 830

Thermal Properties

Melting Onset (Solidus), °C 1320
1590
Specific Heat Capacity, J/kg-K 450
550
Thermal Conductivity, W/m-K 11
8.1
Thermal Expansion, µm/m-K 12
9.1

Otherwise Unclassified Properties

Density, g/cm3 8.2
4.5

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
89 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
1380 to 3220
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
35
Strength to Weight: Axial, points 47
43 to 60
Strength to Weight: Bending, points 34
39 to 48
Thermal Diffusivity, mm2/s 3.0
3.3
Thermal Shock Resistance, points 38
52 to 71