N07041 Nickel vs. Nickel 718
Both N07041 nickel and nickel 718 are nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is nickel 718.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 12 to 50 |
| Fatigue Strength, MPa | 540 | |
| 460 to 760 |
| Shear Strength, MPa | 850 | |
| 660 to 950 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 930 to 1530 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 510 to 1330 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1260 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 450 |
| Thermal Conductivity, W/m-K | 11 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.3 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 140 to 390 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 660 to 4560 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 47 | |
| 31 to 51 |
| Strength to Weight: Bending, points | 34 | |
| 25 to 35 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 3.0 |
| Thermal Shock Resistance, points | 38 | |
| 27 to 44 |