N07041 Nickel vs. SAE-AISI 8630 Steel
N07041 nickel belongs to the nickel alloys classification, while SAE-AISI 8630 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is SAE-AISI 8630 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 12 to 24 |
| Fatigue Strength, MPa | 540 | |
| 260 to 350 |
| Shear Strength, MPa | 850 | |
| 340 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 540 to 680 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 360 to 560 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 39 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 78 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 340 to 840 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 47 | |
| 19 to 24 |
| Strength to Weight: Bending, points | 34 | |
| 19 to 22 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 10 |
| Thermal Shock Resistance, points | 38 | |
| 18 to 23 |