N07041 Nickel vs. C18600 Copper
N07041 nickel belongs to the nickel alloys classification, while C18600 copper belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C18600 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 120 |
| Elongation at Break, % | 14 | |
| 8.0 to 11 |
| Shear Strength, MPa | 850 | |
| 310 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 520 to 580 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 500 to 520 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1070 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 390 |
| Thermal Conductivity, W/m-K | 11 | |
| 280 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 44 to 58 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 1060 to 1180 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 47 | |
| 16 to 18 |
| Strength to Weight: Bending, points | 34 | |
| 16 to 17 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 81 |
| Thermal Shock Resistance, points | 38 | |
| 19 to 20 |