N07041 Nickel vs. C36000 Brass
N07041 nickel belongs to the nickel alloys classification, while C36000 brass belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C36000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 100 |
| Elongation at Break, % | 14 | |
| 5.8 to 23 |
| Shear Strength, MPa | 850 | |
| 210 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 330 to 530 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 140 to 260 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 380 |
| Thermal Conductivity, W/m-K | 11 | |
| 120 |
| Thermal Expansion, µm/m-K | 12 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 25 to 62 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 89 to 340 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 47 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 34 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 37 |
| Thermal Shock Resistance, points | 38 | |
| 11 to 18 |