N07041 Nickel vs. C46400 Brass
N07041 nickel belongs to the nickel alloys classification, while C46400 brass belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C46400 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 100 |
| Elongation at Break, % | 14 | |
| 17 to 40 |
| Shear Strength, MPa | 850 | |
| 270 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 400 to 500 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 160 to 320 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 380 |
| Thermal Conductivity, W/m-K | 11 | |
| 120 |
| Thermal Expansion, µm/m-K | 12 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.0 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 76 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 120 to 500 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 47 | |
| 14 to 17 |
| Strength to Weight: Bending, points | 34 | |
| 15 to 17 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 38 |
| Thermal Shock Resistance, points | 38 | |
| 13 to 16 |