N07041 Nickel vs. C95410 Bronze
N07041 nickel belongs to the nickel alloys classification, while C95410 bronze belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C95410 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 120 |
| Elongation at Break, % | 14 | |
| 9.1 to 13 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 620 to 740 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 260 to 380 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 440 |
| Thermal Conductivity, W/m-K | 11 | |
| 59 |
| Thermal Expansion, µm/m-K | 12 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 57 to 64 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 280 to 630 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 47 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 34 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 16 |
| Thermal Shock Resistance, points | 38 | |
| 22 to 26 |