N07041 Nickel vs. C99750 Brass
N07041 nickel belongs to the nickel alloys classification, while C99750 brass belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C99750 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 130 |
| Elongation at Break, % | 14 | |
| 20 to 30 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 450 to 520 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 220 to 280 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 410 |
| Thermal Expansion, µm/m-K | 12 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 87 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 190 to 300 |
| Stiffness to Weight: Axial, points | 15 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 47 | |
| 15 to 18 |
| Strength to Weight: Bending, points | 34 | |
| 16 to 18 |
| Thermal Shock Resistance, points | 38 | |
| 13 to 15 |