N07716 Nickel vs. 8090 Aluminum

N07716 nickel belongs to the nickel alloys classification, while 8090 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is N07716 nickel and the bottom bar is 8090 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
67
Elongation at Break, % 34
3.5 to 13
Fatigue Strength, MPa 690
91 to 140
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 78
25
Tensile Strength: Ultimate (UTS), MPa 860
340 to 490
Tensile Strength: Yield (Proof), MPa 350
210 to 420

Thermal Properties

Latent Heat of Fusion, J/g 320
400
Maximum Temperature: Mechanical, °C 980
190
Melting Completion (Liquidus), °C 1480
660
Melting Onset (Solidus), °C 1430
600
Specific Heat Capacity, J/kg-K 440
960
Thermal Conductivity, W/m-K 11
95 to 160
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
20
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
66

Otherwise Unclassified Properties

Base Metal Price, % relative 75
18
Density, g/cm3 8.5
2.7
Embodied Carbon, kg CO2/kg material 13
8.6
Embodied Energy, MJ/kg 190
170
Embodied Water, L/kg 280
1160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
16 to 41
Resilience: Unit (Modulus of Resilience), kJ/m3 300
340 to 1330
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
50
Strength to Weight: Axial, points 28
34 to 49
Strength to Weight: Bending, points 24
39 to 50
Thermal Diffusivity, mm2/s 2.8
36 to 60
Thermal Shock Resistance, points 24
15 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.35
93 to 98.4
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 19 to 22
0 to 0.1
Copper (Cu), % 0
1.0 to 1.6
Iron (Fe), % 0 to 11.3
0 to 0.3
Lithium (Li), % 0
2.2 to 2.7
Magnesium (Mg), % 0
0.6 to 1.3
Manganese (Mn), % 0 to 0.2
0 to 0.1
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
0
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 0.2
0 to 0.2
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 1.0 to 1.6
0 to 0.1
Zinc (Zn), % 0
0 to 0.25
Zirconium (Zr), % 0
0.040 to 0.16
Residuals, % 0
0 to 0.15