N07716 Nickel vs. AISI 314 Stainless Steel

N07716 nickel belongs to the nickel alloys classification, while AISI 314 stainless steel belongs to the iron alloys. They have 47% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is AISI 314 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
45
Fatigue Strength, MPa 690
210
Poisson's Ratio 0.29
0.28
Reduction in Area, % 46
57
Shear Modulus, GPa 78
78
Shear Strength, MPa 580
410
Tensile Strength: Ultimate (UTS), MPa 860
590
Tensile Strength: Yield (Proof), MPa 350
230

Thermal Properties

Latent Heat of Fusion, J/g 320
330
Maximum Temperature: Mechanical, °C 980
1100
Melting Completion (Liquidus), °C 1480
1380
Melting Onset (Solidus), °C 1430
1340
Specific Heat Capacity, J/kg-K 440
490
Thermal Conductivity, W/m-K 11
15
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 75
25
Density, g/cm3 8.5
7.7
Embodied Carbon, kg CO2/kg material 13
4.3
Embodied Energy, MJ/kg 190
62
Embodied Water, L/kg 280
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
210
Resilience: Unit (Modulus of Resilience), kJ/m3 300
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 28
21
Strength to Weight: Bending, points 24
20
Thermal Diffusivity, mm2/s 2.8
3.9
Thermal Shock Resistance, points 24
14

Alloy Composition

Aluminum (Al), % 0 to 0.35
0
Carbon (C), % 0 to 0.030
0 to 0.25
Chromium (Cr), % 19 to 22
23 to 26
Iron (Fe), % 0 to 11.3
46.7 to 56.5
Manganese (Mn), % 0 to 0.2
0 to 2.0
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
19 to 22
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0 to 0.045
Silicon (Si), % 0 to 0.2
1.5 to 3.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 1.0 to 1.6
0