N07716 Nickel vs. ASTM B541 Gold

N07716 nickel belongs to the nickel alloys classification, while ASTM B541 gold belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is ASTM B541 gold.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
6.0 to 14
Poisson's Ratio 0.29
0.4
Shear Modulus, GPa 78
38
Shear Strength, MPa 580
410 to 690
Tensile Strength: Ultimate (UTS), MPa 860
670 to 1180
Tensile Strength: Yield (Proof), MPa 350
480 to 900

Thermal Properties

Latent Heat of Fusion, J/g 320
90
Melting Completion (Liquidus), °C 1480
1110
Melting Onset (Solidus), °C 1430
930
Specific Heat Capacity, J/kg-K 440
170
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.7 to 12
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
4.0 to 6.2

Otherwise Unclassified Properties

Density, g/cm3 8.5
17

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
65 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 300
1090 to 3830
Stiffness to Weight: Axial, points 13
3.4
Stiffness to Weight: Bending, points 23
9.0
Strength to Weight: Axial, points 28
11 to 19
Strength to Weight: Bending, points 24
9.8 to 14
Thermal Shock Resistance, points 24
36 to 63

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.35
0
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 19 to 22
0
Copper (Cu), % 0
13.5 to 15.5
Gold (Au), % 0
70.5 to 72.5
Iron (Fe), % 0 to 11.3
0
Manganese (Mn), % 0 to 0.2
0
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
0
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0
Platinum (Pt), % 0
8.0 to 9.0
Silicon (Si), % 0 to 0.2
0
Silver (Ag), % 0
4.0 to 5.0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 1.0 to 1.6
0
Zinc (Zn), % 0
0.7 to 1.3
Residuals, % 0
0 to 0.4