N07716 Nickel vs. AWS BAg-19

N07716 nickel belongs to the nickel alloys classification, while AWS BAg-19 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is AWS BAg-19.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
74
Poisson's Ratio 0.29
0.37
Shear Modulus, GPa 78
27
Tensile Strength: Ultimate (UTS), MPa 860
140

Thermal Properties

Latent Heat of Fusion, J/g 320
120
Melting Completion (Liquidus), °C 1480
890
Melting Onset (Solidus), °C 1430
760
Specific Heat Capacity, J/kg-K 440
250
Thermal Expansion, µm/m-K 13
20

Otherwise Unclassified Properties

Density, g/cm3 8.5
10

Common Calculations

Stiffness to Weight: Axial, points 13
4.0
Stiffness to Weight: Bending, points 23
14
Strength to Weight: Axial, points 28
3.8
Strength to Weight: Bending, points 24
5.8
Thermal Shock Resistance, points 24
6.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.35
0
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 19 to 22
0
Copper (Cu), % 0
6.6 to 7.9
Iron (Fe), % 0 to 11.3
0
Lithium (Li), % 0
0.15 to 0.3
Manganese (Mn), % 0 to 0.2
0
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
0
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 0.2
0
Silver (Ag), % 0
92 to 93
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 1.0 to 1.6
0
Residuals, % 0
0 to 0.15